电压对电刷镀三价铬镀层性能的影响

在45钢表面电刷镀得到三价铬镀层,镀液组成和工艺条件为:Cr2(SO4)36H2O 0.4 mol/L,甲酸铵0.5 mol/L,氨基乙酸0.5 mol/L,H3BO30.6 mol/L,NaH2PO2 H2O 0.3 mol/L,pH=1.5,温度50°C,镀笔移动速率15 cm/s。研究了电压对镀铬层显微结构、表面粗糙度、厚度、显微硬度和耐磨性的影响。随电压增大,镀层厚度增大,显微硬度和耐磨性均先提高后降低。电压为14 V时,镀层的表面平整,粗糙度为2.387μm,显微硬度为602 HV,耐磨性最好。     

Triphenylphosphonium (TPP)-Based Antioxidants: A New Perspective on Antioxidant Design

Mitochondrial oxidative damage and dysfunction contribute to a wide range of human diseases. Considering the limitation of conventional antioxidants and that mitochondria are the main source of reactive oxygen species (ROS) which induce oxidative damage, mitochondria-targeted antioxidants which can selectively block mitochondrial oxidative damage and prevent various types of cell death have been widely developed. As a lipophilic cation, triphenylphosphonium (TPP) has been commonly used in designing mitochondria-targeted antioxidants. Conjugated with the TPP moiety, antioxidants can achieve more than 1000-fold higher mitochondrial concentration depending on cell membrane potentials and mitochondrial membrane potentials. Herein we discuss the deficiencies of conventional antioxidants and the advantages of mitochondrial targeting, and review various types of TPP-based mitochondria-targeted antioxidants. These provide theoretical and background support for the design of new anti-oxidant.     

Ni-Foam Structured Ni-Phyllosilicate Ensemble as an Efficient Monolithic Catalyst for CO2 Methanation

This work proposed a new path to synthesize Ni-phyllosilicate through the reaction of nickel hydroxide and silica sol on the surface of Ni-foam to form the monolithic Ni-phyllosilicate/Ni-foam catalyst. Ni-phyllosilicate could reprint the morphology of nickel hydroxid and firmly anchor on the framework of Ni-foam, which obtained fine Ni particles of 2.8 nm after reduction in H₂ at 650 °C, resulting in high catalytic activity for CO₂ methanation. In addition, the Ni-phyllosilicate/Ni-foam catalyst showed high long-term stability in a 100 h-lifetime test owing to the combined effects of surface confinement of Ni-phyllosilicate, firm anchoring between Ni-phyllosilicate and Ni-foam, as well as the high heat transfer property of Ni-foam.

Graphical Abstract

     

Toughness enhancement and equivalent initial fracture toughness of cementitious composite reinforced with aligned steel fibres

Based on theoretical analysis and numerical simulation, the impact of steel fibres on the stress intensity factor (SIF) at the crack tip for cementitious composite was studied. The enhanced toughness of steel fibre reinforced cementitious composite (SFRC) in resisting cracks was explained by the decrement of SIF caused by steel fibre inclusions at the crack tip of the composite. The equivalent initial fracture toughness was used to characterize the crack initiation of SFRC. A simplified method for determining the of SFRC was proposed based on a linear regression method. Fracture tests were conducted on three‐point bending notched beams with different steel fibre volume fractions and specimen sizes to study the crack initiation behaviour of aligned steel fibre reinforced cementitious composite (ASFRC). of ASFRC was calculated, and the size effect of was analysed. The results showed that slightly increased with the steel fibre volume fraction and gradually became stable. For the tested specimens, whose heights varied between 40 and 100 mm, the specimen size had little impact on the .     

釉面分相对无铅CuO-MnO2系金属光泽釉的影响

以钙系生料釉为基础,引入结晶剂CuO、MnO₂制备无铅CuO-MnO₂系金属光泽釉;结合XRD、SEM-EDS进行物相组成定性分析和显微结构表征,系统探究外加TiO₂、V₂O₅以及玻璃粉对金属光泽釉釉面分相的影响。研究表明:一定量的TiO₂、V₂O₅引入能有效促进釉面的分相,将玻璃粉部分替换基础釉中的钾长石能使得釉熔体的高温粘度降低,并进一步加剧釉面分相,促进CuMn₂O₄铜锰尖晶石在釉层表面的析出和富集;当TiO₂引入量为2%,V₂O₅引入量为1%,玻璃粉引入量为25%(同为质量分数)时,金属光泽釉釉面效果最佳。